Dental adhesive

ABSTRACT

A one-part self-etching, self-priming dental adhesive having a pH of at most 2, which comprises an aqueous mixture containing
         (i) one or more polymerizable monomers optionally containing an acidic group,   (ii) optionally one or more organic or inorganic acids,   (iii) a polymerization initiator, and   (iv) a thermal polymerisation inhibitor of the following formula (I):       

     
       
         
         
             
             
         
       
         
         
           
             
               
                 wherein 
                 R′ 1  represents
               a hydrogen atom, or a saturated hydrocarbon group having 1 to 18 carbon atoms.   
             
                 R′ 2 , which may be the same or different if more than one R′ 2  is present, independently represent
               a saturated hydrocarbon group having 1 to 18 carbon atoms, and   
             
                 c represents an integer of from 1 to 4.

FIELD OF THE INVENTION

The present invention relates to a one-part self-etching, self-priming dental adhesive having improved storage stability and low toxicity. Moreover, the present invention also relates to the use of a specific thermal polymerisation inhibitor in a one-part self-etching, self-priming dental adhesive having a pH of at most 2.

BACKGROUND OF THE INVENTION

One-part self-etching, self-priming dental adhesive compositions known from the prior art typically contain a mixture of an acid, a polymerizable monomer and an initiator system in a suitable solvent. The acidity of the mixture must be adapted to provide sufficient etching activity on dentin and enamel surfaces. However, an increased acidity leads to a complex stability problem due to the activation of chemical bonds of the functional components of the mixture. Specifically, ester bonds present in the polymerizable monomers may be solved under acid catalysis. Moreover, the initiator system may be activated in the acidic medium leading to premature polymerization of the mixture.

As a result of the stability problem of the mixture, the storage stability at room temperature of commercial one-part self-etching, self-priming dental adhesive compositions known from the prior art may be insufficient. Accordingly, conventional commercial one-part self-etching, self-priming dental adhesive compositions must be stored in a refrigerator in order to avoid deterioration by solvolysis or polymerization. As an Example, the commercial composition “iBond Gluma inside” may be mentioned, which has a low thermal stability when stored at temperatures of 37° C. or 50° C. due to premature polymerization within less than two weeks, which is indicative of an insufficient thermal stability at room temperature for all practical purposes.

EP-A 1 548 021 suggests hydrolysis stable one-part self-etching, self-priming dental adhesive compositions containing specific monomers having improved resistance against hydrolysis under acidic conditions. In order to improve the stability of the initiator system, EP-A 1 548 021 suggests a stabilizer such as hydroquinone monomethylether, 2,6-di-tert.-butyl-p-cresol, tetramethyl piperidine N-oxyl radical and galvanoxyl radical. However, generic one-part self-etching, self-priming dental adhesive composition known from EP-A 1 548 021 still require improvement of the thermal stability at storage for attaining a stability of at least 10 days at 60° C. required. Moreover, hydroquinone is an allergenic compound imparting undesirable toxic properties to a dental adhesive composition.

SUMMARY OF THE INVENTION

It is a problem of the present invention to provide a one-part self-etching, self-priming dental adhesive composition having a low toxicity and thermal stability at storage of at least 10 days at 60° C.

The present invention provides a one-part self-etching, self-priming dental adhesive having a pH of at most 2, which comprises an aqueous mixture containing

-   -   (i) one or more polymerizable monomers optionally containing an         acidic group,     -   (ii) optionally one or more organic or inorganic acids,     -   (iii) a polymerization initiator, and     -   (iv) a thermal polymerisation inhibitor of the following formula         (I):

-   -   -   wherein         -   R′₁ represents             -   a hydrogen atom, or a saturated hydrocarbon group having                 1 to 18 carbon atoms.         -   R′₂, which may be the same or different if more than one R′₂             is present, independently represent             -   a saturated hydrocarbon group having 1 to 18 carbon                 atoms, and         -   c represents an integer of from 1 to 4.

The present invention is based on the recognition that an aqueous mixture containing one or more polymerizable monomers optionally containing an acidic group, one or more organic or inorganic acids, and a polymerization initiator is particularity problematic with regard to polymerization whereby conventional stabilizers such as hydroquinone monomethylether, 2,6-di-tert.-butyl-p-cresol, tetramethyl piperidine N-oxyl radical and galvanoxyl radical provide an insufficient effect for attaining a high storage stability.

The present invention is furthermore based on the recognition that a specific class of water insoluble stabilizers provides a surprising stabilizing effect in an acidic aqueous mixture so that a one-part self-etching, self-priming dental adhesive having a pH of at most 2 may be provided which has an excellent storage stability due to an improved resistance against premature polymerization.

Accordingly, the present invention also relates to the of a thermal polymerisation inhibitor of formula (I) in a one-part self-etching, self-priming dental adhesive having a pH of at most 2.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The dental adhesive composition according to the present invention contains a water-insoluble thermal polymerisation inhibitor of formula (I).

Preferably, the saturated hydrocarbon group which may be present as R′₁ or R′₂ in formula (I) represents a straight chain or branched C₁₋₁₈, alkyl group or a C₃₋₈ cycloalkyl group optionally substituted by one or more C₁₋₅ alkyl groups or a C₄₋₁₈ cycloalkylalkyl group optionally substituted by one or more C₁₋₅ alkyl groups.

Preferably, R′₁ represents a straight chain or branched C₁₋₁₈ alkyl group. In a preferred embodiment, R′₁ is hydrogen or a tert.-butyl group.

R′₂ in formula (I) is believed to provide a steric effect due to the bulky nature of the substituent in this position. Therefore, at least one R′₂ in formula (I) is a saturated hydrocarbon group having 1 to 18 carbon atoms. Accordingly, in a specific embodiment, at least one R′₂ in formula (I) represents a branched C₃₋₁₈ alkyl group or a C₃₋₁₈ cycloalkyl group optionally substituted by one or more C₁₋₅ alkyl groups or a C₄₋₁₈ cycloalkylalkyl group optionally substituted by one or more C₁₋₅ alkyl groups. More specifically, at least one R′₂ in formula (I) preferably represents a branched C₃₋₁₈ alkyl group or a C₃₋₁₈ cycloalkyl group optionally substituted by one or more C₁₋₅ alkyl groups. Even more specifically, at least one R′₂ in formula (I) preferably represents a branched C₃₋₁₈ alkyl group. In a further preferred embodiment, R′₂ is a tert.-butyl group.

c represents an integer of from 1 to 4, preferably 1 or 2. In a specific embodiment, c is 1.

Most preferably, the inhibitor is tert.-butyl hydroquinone (TBHQ) or tert.-butyl hydroxyanisole (BHA).

Preferably, the inhibitor is contained in the dental adhesive composition in an amount of from 0.01 to 0.5 mol %, more preferably in an amount of from 0.05 to 0.3 mol %.

In a preferred embodiment, The present invention provides a one-part self-etching, self-priming dental adhesive having a pH of at most 2, which comprises an aqueous mixture containing

-   -   (i) one or more polymerizable monomers optionally containing an         acidic group,     -   (ii) optionally one or more organic or inorganic acids,     -   (iii) a polymerization initiator, and     -   (iv) a thermal polymerisation inhibitor of the following         formula:

-   -   -   R′₁ represents             -   a hydrogen atom, or a saturated hydrocarbon group having                 1 to 18 carbon atoms.         -   R′₂ represents             -   a saturated hydrocarbon group having 1 to 18 carbon                 atoms.

The dental adhesive composition according to the present invention contains a polymerizable monomers optionally containing an acidic group. Preferably, the polymerizable monomer is a polymerizable acidic phosphoric acid ester monomer of the following formula (A):

wherein the moieties Y independent from each other represent a hydrogen atom or a moiety of the following formula (Y)

wherein Z₁ is COOR¹⁰, COSR²⁰, CON(R¹⁰)₂, CONR¹⁰R²⁰, or CONHR¹⁰, wherein R¹⁰ and R²⁰ independently represent a hydrogen atom, a C₁₋₁₈ alkyl group optionally substituted by a C₃₋₈ cycloalkyl group, an optionally substituted C₃₋₈ cycloalkyl group, an optionally substituted C₄₋₁₈, aryl or heteroaryl group, an optionally substituted C₅₋₁₈ alkylaryl or alkylheteroaryl group, or an optionally substituted C₇₋₃₀ aralkyl group, whereby two R₁ residues may form together with the adjacent nitrogen atom to which they are bound a 5- to 7-membered heterocyclic ring which may contain further nitrogen atoms or an oxygen atoms, and whereby the optionally substituted groups may be substituted by 1 to 5 C₁₋₅ alkyl group(s); L represents an (a+b)-valent organic residue (whereby b is 1 when Y in formula (A) is within the round bracketsis) containing 2 to 45 carbon atoms and optionally heteroatoms such as oxygen, nitrogen and sulfur atoms, the carbon atoms including a+b carbon atoms selected from primary and secondary aliphatic carbon atoms, secondary alicyclic carbon atoms, and aromatic carbon atoms, each of said a+b carbon atoms linking a phosphate or 2-(oxa-ethyl)acryl derivative group; a is an integer of from 1 to 10, preferably 1 to 5; b is an integer of from 1 to 10, preferably 1 to 5; provided that at least one Y is not hydrogen. The preparation of such monomers is known from EP-A 1 548 021.

The dental adhesive may also contain polymerisable acidic monomers selected from the group consisting of

(b1) polymerisable acidic monomers of the following formula (B):

wherein R₁ and R₂ independently represent a hydrogen atom, an optionally substituted C₁₋₁₈ alkyl group, an optionally substituted C₃₋₁₈ cycloalkyl group, an optionally substituted C₅₋₁₈ aryl or heteroaryl group, an optionally substituted C₅₋₁₈ alkylaryl or alkylh3eteroaryl group, an optionally substituted C₇₋₃₀ aralkyl group, whereby the optionally substituted groups may be substituted by 1 to 5 C₁₋₅ alkyl group(s);

L₁ represents a (c+d) valent organic residue containing 2 to 45 carbon atoms and optionally heteroatoms such as oxygen, nitrogen and sulfur, the carbon atoms including c+d carbon atoms selected from primary and secondary aliphatic carbon atoms, secondary alicyclic carbon atoms, and aromatic carbon atoms, each of said c+d carbon atoms linking a phosphonate or optionally substituted acrylamido group; and

c and d independently represent integers of from 1 to 10; (b2) polymerisable acidic monomers of the following formula (C):

wherein Z₂ independently has the same meaning as defined for Z₁; L₂ represents an (e+f) valent organic residue containing 2 to 45 carbon atoms and optionally heteroatoms such as oxygen, nitrogen and sulfur-atoms, the carbon atoms including e+f carbon atoms selected from primary and secondary aliphatic carbon atoms, secondary alicyclic carbon atoms, and aromatic carbon atoms, each of said e+f carbon atoms linking a sulphonate or optionally substituted 2-(oxa-ethyl)acryl derivative group; and e and f independently represent an integer of from 1 to 10; (b3) acidic monomers of the following formula (D):

wherein R₃ and R₄ independently represent a hydrogen atom, an optionally substituted C₁₋₁₈ alkyl group, an optionally substituted C₃₋₁₈ cycloalkyl group, an optionally substituted C₅₋₁₈ aryl or heteroaryl group, an optionally substituted C₅₋₁₈ alkylaryl or alkylheteroaryl group, an optionally substituted C₇₋₃₀ aralkyl group, whereby the optionally substituted groups may be substituted by 1 to 5 C₁₋₅ alkyl group(s) L₃ represents a (g+h) valent valent organic residue containing 2 to 45 carbon atoms and optionally heteroatoms such as oxygen, nitrogen and sulfur atoms, the carbon atoms including g+h carbon atoms selected from primary and secondary aliphatic carbon atoms, secondary alicyclic carbon atoms, and aromatic carbon atoms, each of said g+h carbon atoms linking a sulphonate or optionally substituted acrylamido group; and g and h independently represent integers of from 1 to 10.

In a preferred embodiment, the dental adhesive contains a polymerizable monomer characterized by one of the following formulas:

wherein Z is Z₁ as defined above, (R₄) is an optionally substituted alkylene group, and

n is an integer.

In a further preferred embodiment, the dental adhesive contains a polymerizable monomer characterized by one of the following formulas:

In a still further preferred embodiment, the dental adhesive contains a polymerizable monomer characterized by one of the following formulas:

wherein R₅ and R₆ independently represent a hydrogen atom or a substituted, a C₁ to C₁₈ alkyl group, an optionally substituted C₃₋₁₈ cycloalkyl group, an optionally substituted C₅₋₁₈ aryl or heteroaryl group, an optionally substituted C₅₋₁₈ alkylaryl or alkylheteroaryl group, an optionally substituted C₇₋₃₀ aralkyl group, R₇ represents a divalent substituted or unsubstituted organic residue having from 1 to 45 carbon atoms, whereby said organic residue may contain from 1 to 14 oxygen and/or nitrogen atoms and is selected from a C₁ to C₁₈ alkylene group wherein from 1 to 6-CH₂-groups may be replaced by a —N—(C═O)—CR₉═CH₂ group wherein R₁ is a hydrogen atom or a C₁ to C₁₈ alkyl group, a divalent substituted or unsubstituted C₃ to C₁₈ cycloalkyl or cycloalkylene group, a divalent substituted or unsubstituted C₄ to C₁₈ aryl or heteroaryl group, a divalent substituted or unsubstituted C₅ to C₁₈ alkylaryl or alkylheteroaryl group, a divalent substituted or unsubstituted C₇ to C₃₀ aralkyl group, and a divalent substituted or unsubstituted C₂ to C₄₅ mono-, di- or polyether group having from 1 to 14 oxygen atoms, R₈ represents a saturated di- or multivalent substituted or unsubstituted C₂ to C₁₈ hydrocarbon group, a saturated di- or multivalent substituted or unsubstituted cyclic C₃ to C₁₈ hydrocarbon group, a di- or multivalent substituted or unsubstituted C₄ to C₁₈ aryl or heteroaryl group, a di- or multivalent substituted or unsubstituted C₂ to C₁₈ alkylaryl or alkylheteroaryl group, a di- or multivalent substituted or unsubstituted C₇ to C₃₀ aralkyl group, or a di- or multivalent substituted or unsubstituted C₂ to C₄₅ mono-, di-, or polyether residue having from 1 to 14 oxygen atoms, and n is an integer.

The dental adhesive may also contain a mono-, bis- or poly(meth) acrylamide characterized by one of the following formulas:

The dental adhesive may also contain acrylic acid or methacrylic acid as polymerizable monomers containing an acidic group.

The dental adhesive according to the present invention may contain polymerizable monomers in an amount of from 5 to 90 wt-%, preferably in an amount of from 20 to 70 wt. %.

The aqueous mixture may further contain an organic water soluble solvent selected from the group of alcohols and ketones such as ethanol, propanol, butanol, acetone, methyl ethyl ketone.

A dental composition according to the present invention may include further acids whereby the pH of the composition may be easily adjusted. Examples of suitable acids are sulfuric acid, phosphoric acid, hydrochloric acid and the like. In a specific example, a further acid which is not-polymerizable is added for adjusting the pH.

The polymerization initiator may be a photo initiator such as camphor quinone.

The dental adhesive may further contains an inorganic filler and/or an organic filler; preferably the filler is a nanofiller.

A one-pack composition means that the composition of the present invention is contained in only one container which may be stored and allows application of the composition without any mixing and without any special equipment before the application.

Self-etching means that the dental adhesive composition of the present invention may be applied to a tooth without any preliminarily etching of enamel in a separate method step. Particularly, the polymerizable phosphoric acid ester derivative of the present invention allows the preparation of a dental composition which is hydrolysis stable for at least one week at a storage temperature of 50° C., whereby after such storage the bond strength of an adhesive prepared from such a dental composition to enamel and/or dentin is at least 10 MPa, preferably 15 MPa. Due to the high thermal stability of the composition of the present invention a one-part self-etching and self-priming system which has excellent shelf-life may be prepared.

The invention will now be further illustrated with reference to the following examples

EXAMPLES Test Formulation Containing Different Inhibitors

A series of test formulations containing different thermal polymerization inhibitors was prepared in order to illustrate the surprising thermal stability of a dental adhesive composition according to the present invention. The standard composition was used as follows.

Component Content wt.-% BAP 63156 BAA-TCD 21052 DHPOBA analog 5415 2-Acrylamido-2-methyl- 4375 propansulfonsäure (AMPS) Camphor Quinone 1282 TPO 3229 DMABE 1491 Total 100000 Active Matrix 55 Acrylic acid 9 Water 36 Total 100

The following comparative inhibitors were tested:

(i) hydroquinone (HQ), (ii) hydroquinone monomethylether (HQME), (iii) Bisphenol A, (iv) Propyl gallate (PG)

The following inhibitors according to the present invention were tested:

(vii) tert-Butylhydroquinone (TBHQ), and (viii) tert.-Butylhydroxyanisol (BHA).

Test formulations containing different inhibitors or inhibitor concentrations were stored in Prime&Bond NT bottles (Dentsply DeTrey) at 60° C. until thermal polymerization. The bottles were daily examined by shaking the bottle, whereby the acoustical test turned out to be rather sensitive, and by taking a sample with a pipette. When polymerization seemed to have occurred or after a certain minimum storage time (20 days) the bottles were sliced open and the solution were examined visually.

According to the results of the above described Arrhenius investigation at least a thermal stability of about 11 days at 6.0° C. is necessary so that the dental adhesive composition may be stored at room temperature.

Results

The Test Formulation containing different inhibitors in different amounts, was investigated regarding its thermal stability by storing these formulations at 60° C. The samples were daily examined. In case of polymerization a gel or a solid, polymerized body was observed.

The dark shaded columns represent formulations with inhibitors, respectively inhibitor concentrations, which were polymerized after the depicted time at 60° C. The light shaded columns represent formulations, which were not polymerized until the depicted time. Usually after 20 days the investigation was terminated. In the comparison, hydroquinone (HQ) was used in an amount of 0.15 mol % showing some stabilization effect. However, hydroquinone is an allergenic compound and therefore undesirable for use in a generic dental composition. Hydroquinone monomethylether (HQME) as well as BHT failed to provide a sufficient thermal stability.

(i) Hydrochinone (HQ)—Reference Inhibitor

(light shaded columns—formulation is not polymerised up to the recorded time; dark shaded column: formulation is polymerized after the recorded time)

After slicing open the samples containing 0.49 and 0.697 mol % HQME, small pieces of gel were found at the bottom, which were not detected before by shaking or by the examination with the pipette.

After slicing open the sample with 0.193 mol % TBC some pieces of gel were found at the bottom, which were not detected before by shaking or by the examination with the pipette.

(the dark shaded columns indicate that the formulation is polymerized after the recorded time)

The dark shaded columns indicate that the formulation is polymerized after the recorded time

(vii) tert.-Butylhydrochinone (TBHQ)—Inhibitor of the Invention

After 14 days and after 20 days at 60° C. the bottles were sliced open, the contents was investigated and filled in a new bottle, which was stored again at 60° C. No hints of a polymerization were found.

After 20 days at 60° C. the bottles were sliced open again and the contents was investigated. Only in case of the lowest TBHQ percentage of 0.013 mol % polymerization was found. This was not detected before by the daily examination.

After 14 days at 60° C. all bottles were sliced open, the contents was investigated and filled in a new bottle, which was stored again at 60° C. The sample with 0.047 mol % showed after 14 days at 60° C. some pieces of gel, which were not detected before by shaking or by the examination with the pipette. After 20 days at 60° C. the bottles were again sliced open. No indication of polymerization for the samples containing 0.096 mol % and 0.147 mol % were found. The formulation with 0.047 mol % again contains some small pieces of gel.

Example 1

0.6945 g N,N′-Bisacrylamido-N,N′-diethyl-1,3-propane, 0.2315 g 3,(4),8,(9)-bis(acrylamido methyl) tricyclo-5.2.1.0^(2,6) decane, 0.0595 g Ethyl 2-[12-dihydrogen phosphoryl-12,2-dioxamidecyl]acrylate, 0.0481 g 2-Acrylamido-2-methyl-propane-sulfonic acid, 0.0141 g camphor quinone, 0.0355 g bis(2,4,6-trimethylbenzoyl)-phenyl phosphine oxide, 0.0164 g dimethylamino benzoic acid ethyl ester and 0.003 g 2-tert-Butylhydroquinone were dissolved in a solvent mixture composed of 0.1800 g acrylic acid and 0.7200 g water.

The adhesive does not polymerise after storage for 20 days at 60° C.

Example 2

0.6940 g N,N′-Bisacrylamido-N,N′-diethyl-1,3-propane, 0.2313 g 3,(4),8,(9)-bis(acrylamido methyl) tricyclo-5.2.1.0^(2,6) decane, 0.0595 g Ethyl 2-[12-dihydrogen phosphoryl-12,2-dioxamidecyl]acrylate, 0.0481 g 2-Acrylamido-2-methyl-propane-sulfonic acid, 0.0141 g camphor quinone, 0.0355 g bis(2,4,6-trimethylbenzoyl)-phenyl phosphine oxide, 0.0164 g dimethylamino benzoic acid ethyl ester and 0.0011 g 2-tert.-butyl-4-methoxyphenol were dissolved in a solvent mixture composed of 0.1800 g acrylic acid and 0.7200 g water. The adhesive does not polymerise after storage for 20 days at 60° C.

Comparative Example 1

0.6931 g N,N′-Bisacrylamido-N,N′-diethyl-1,3-propane, 0.2310 g 3,(4),8,(9)-bis(acrylamido methyl) tricyclo-5.2.1.0^(2,6) decane, 0.0594 g ethyl 2-[12-dihydrogen phosphoryl-12,2-dioxamidecyl]acrylate, 0.0480 g 2-Acryiamido-2-methyl-propane-sulfonic acid, 0.0141 g camphor quinone, 0.0354 g bis(2,4,6-trimethylbenzoyl)-phenyl phosphine oxide, 0.0164 g dimethylamino benzoic acid ethyl ester and 0.0026 g hydroquinone monomethyl ether were dissolved in a solvent mixture composed of 0.1800 g acrylic acid and 0.7200 g water.

The adhesive polymerises after storage for 1 day at 60° C.

Comparative Example 2

0.6882 g N,N′-Bisacrylamido-N,N′-diethyl-1,3-propane, 0.2294 g 3,(4),8,(9)-bis(acrylamido methyl) tricyclo-5.2.1.0^(2,6) decane, 0.0590 g Ethyl 2-[12-dihydrogen phosphoryl-12,2-dioxamidecyl]acrylate, 0.0477 g 2-Acrylamido-2-methyl-propane-sulfonic acid, 0.0140 g camphor quinone, 0.0352 g bis(2,4,6-trimethylbenzoyl)-phenyl phosphine oxide, 0.0162 g dimethylamino benzoic acid ethyl ester and 0.0103 g 2,6-di-tert.-butyl-4-cresol were dissolved in a solvent mixture composed of 0.1800 g acrylic acid and 0.7200 g water. The adhesive polymerises after storage for 2 days at 60° C. 

1. One-part self-etching, self-priming dental adhesive having a pH of at most 2, which comprises an aqueous mixture containing (i) one or more polymerizable monomers optionally containing an acidic group, (ii) optionally one or more organic or inorganic acids, (iii) a polymerization initiator, and (iv) a thermal polymerisation inhibitor of the following formula (I):

wherein R′₁ represents a hydrogen atom, or a saturated hydrocarbon group having 1 to 18 carbon atoms. R′₂, which may be the same or different if more than one R′₂ is present, independently represent a saturated hydrocarbon group having 1 to 18 carbon atoms, and c represents an integer of from 1 to
 4. 2. The adhesive according to claim 1, wherein the thermal polymerisation inhibitor of formula (I) is a compound of the following formula:

wherein R′₁ represents a hydrogen atom, or a saturated hydrocarbon group having 1 to 18 carbon atoms, and R′₂ represents a saturated hydrocarbon group having 1 to 18 carbon atoms.
 3. The adhesive according to claim 1 or 2, which is stable at storage for at least 10 days at 60° C.
 4. The dental adhesive according to claim 1, 2 or 3, wherein the saturated hydrocarbon group is a straight chain or branched C₁₋₁₈ alkyl group or a C₃₋₁₈ cycloalkyl group optionally substituted by one or more C₁₋₅ alkyl groups or a C₁₋₁₈ cycloalkylalkyl group optionally substituted by one or more C₁₋₅ alkyl groups.
 5. The dental adhesive according to claim 1, 2 or 3, wherein the saturated hydrocarbon group of R′₂ is a branched C₁₋₁₈ alkyl group.
 6. The dental adhesive according to any one of the preceding claims, wherein R′₂ is a tert.-butyl group.
 7. The dental adhesive according to any one of the preceding claims, wherein the inhibitor is TBHQ or BHA.
 8. The dental adhesive according to any one of the preceding claims, wherein the inhibitor is contained in an amount of from 0.01 to 0.5 mol %.
 9. The dental adhesive according to any one of the preceding claims, wherein the one or more polymerizable monomers comprises (a) a polymerizable acidic phosphoric acid ester monomer of the following formula (A):

wherein the moieties Y independent from each other represent a hydrogen atom or a moiety of the following formula (Y)

wherein Z₁ is COOR¹⁰, COSR²⁰, CON(R¹⁰)₂, CONR¹⁰R²⁰, or CONHR¹⁰, wherein R¹⁰ and R²⁰ independently represent a hydrogen atom,  a C₁₋₁₈ alkyl group optionally substituted by a C₃₋₈ cycloalkyl group,  an optionally substituted C₃₋₈ cycloalkyl group, an optionally substituted C₄₋₁₈ aryl or heteroaryl group,  an optionally substituted C₅₋₁₈ alkylaryl or alkylheteroaryl group, or  an optionally substituted C₇₋₃₀ aralkyl group, whereby two R₁, residues may form together with the adjacent nitrogen atom to which they are bound a 5- to 7-membered heterocyclic ring which may contain further nitrogen atoms or an oxygen atoms, and whereby the optionally substituted groups may be substituted by 1 to 5 C₁₋₅ alkyl group(s); L represents an (a+b)-valent organic residue (whereby b is 1 when Y in formula (A) is within the round bracketsis) containing 2 to 45 carbon atoms and optionally heteroatoms such as oxygen, nitrogen and sulfur atoms, the carbon atoms including a+b carbon atoms selected from primary and secondary aliphatic carbon atoms, secondary alicyclic carbon atoms, and aromatic carbon atoms, each of said a+b carbon atoms linking a phosphate or 2-(oxa-ethyl)acryl derivative group; a is an integer of from 1 to 10, preferably 1 to 5; b is an integer of from 1 to 10, preferably 1 to 5; provided that at least one Y is not hydrogen.
 10. The dental adhesive according to any one of the preceding claims, wherein the one or more polymerizable monomers comprises (b) one or more polymerisable acidic monomers selected from the group consisting of (b1) polymerisable acidic monomers of the following formula (B):

wherein R₁ and R₂ independently represent a hydrogen atom, an optionally substituted C₁₋₁₈ alkyl group, an optionally substituted C₃₋₁₈ cycloalkyl group, an optionally substituted C₅₋₁₈ aryl or heteroaryl group, an optionally substituted C₅₋₁₈ alkylaryl or alkylheteroaryl group, an optionally substituted C₇₋₃₀ aralkyl group, whereby the optionally substituted groups may be substituted by 1 to 5 C₁—, alkyl group(s); L₁ represents a (c+d) valent organic residue containing 2 to 45 carbon atoms and optionally heteroatoms such as oxygen, nitrogen and sulfur, the carbon atoms including c+d carbon atoms selected from primary and secondary aliphatic carbon atoms, secondary alicyclic carbon atoms, and aromatic carbon atoms, each of said c+d carbon atoms linking a phosphonate or optionally substituted acrylamido group; and c and d independently represent integers of from 1 to 10; (b2) polymerisable acidic monomers of the following formula (C):

wherein Z₂ independently has the same meaning as defined for Z₁; L₂ represents an (e+0 valent organic residue containing 2 to 45 carbon atoms and optionally heteroatoms such as oxygen, nitrogen and sulfur atoms, the carbon atoms including e+f carbon atoms selected from primary and secondary aliphatic carbon atoms, secondary alicyclic carbon atoms, and aromatic carbon atoms, each of said e+f carbon atoms linking a sulphonate or optionally substituted 2-(oxa-ethyl)acryl derivative group; and e and f independently represent an integer of from 1 to 10; (b3) acidic monomers of the following formula (D):

wherein R₃ and R₄ independently represent a hydrogen atom, an optionally substituted C₁₋₁₈ alkyl group, an optionally substituted C₃₋₁₈ cycloalkyl group, an optionally substituted C₅₋₁₈ aryl or heteroaryl group, an optionally substituted C₅₋₁₈ alkylaryl or alkylheteroaryl group, an optionally substituted C₇₋₃₀ aralkyl group, whereby the optionally substituted groups may be substituted by 1 to 5 C₁₋₅ alkyl group(s) L₃ represents a (g+h) valent organic residue containing 2 to 45 carbon atoms and optionally heteroatoms such as oxygen, nitrogen and sulfur atoms, the carbon atoms including g+h carbon atoms selected from primary and secondary aliphatic carbon atoms, secondary alicyclic carbon atoms, and aromatic carbon atoms, each of said g+h carbon atoms linking a sulphonate or optionally substituted acrylamido group; and g and h independently represent integers of from 1 to
 10. 11. The dental adhesive according to any one of the preceding claims, wherein the aqueous mixture further contains an organic water soluble solvent selected from the group of alcohols and ketones such as ethanol, propanol, butanol, acetone, methyl ethyl ketone.
 12. The dental adhesive according to any one of the preceding claims, wherein the polymerizable monomer of component (i) is characterized by one of the following formulas:

wherein Z is Z₁ as defined in claim 7 (R₄) is an optionally substituted alkylene group, and n is an integer.
 13. The dental adhesive according to any one of the preceding claims, wherein said acidic polymerizable monomer is characterized by one of the following formulas:


14. The dental adhesive according to any one of the preceding claims, wherein the polymerizable monomer of component (i) is characterized by one of the following formulas:

wherein R₅ and R₆ independently represent a hydrogen atom or a substituted a C₁ to C₁₈ alkyl group, an optionally substituted C₃₋₁₈ cycloalkyl group, an optionally substituted C₃₋₁₈ aryl or heteroaryl group, an optionally substituted C₅₋₁₈ alkylaryl or alkylheteroaryl group, an optionally-substituted C₇₋₃₀ aralkyl group, R₇ represents a a divalent substituted or unsubstituted organic residue having from 1 to 45 carbon atoms, whereby said organic residue may contain from 1 to 14 oxygen and/or nitrogen atoms and is selected from a C₁ to C₁₈ alkylene group wherein from 1 to 6-CH₂-groups may be replaced by a —N—(C═O)—CR₉═CH₂ group wherein R₉ is a hydrogen atom or a C₁ to C₁₈ alkyl group, a divalent substituted or unsubstituted C₃ to C₁₈ cycloalkyl or cycloalkylene group, a divalent substituted or unsubstituted C₄ to C₁₈ aryl or heteroaryl group, a divalent substituted or unsubstituted C₅ to C₁₈ alkylaryl or alkylheteroaryl group, a divalent substituted or unsubstituted C₇ to C₃₀ aralkyl group, and a divalent substituted or unsubstituted C₂ to C₄₅ mono-, di- or polyether group having from 1 to 14 oxygen atoms, R₈ represents a saturated di- or multivalent substituted or unsubstituted C₂ to C₁₈ hydrocarbon group, a saturated di- or multivalent substituted or unsubstituted cyclic C₃ to C₁₈ hydrocarbon group, a di- or multivalent substituted or unsubstituted C₄ to C₁₈ aryl or heteroaryl group, a di- or multivalent substituted or unsubstituted C₅ to C₁₈ alkylaryl or alkylheteroaryl group, a di- or multivalent substituted or unsubstituted C₇ to C₃₀ aralkyl group, or a di- or multivalent substituted or unsubstituted C₂ to C₄₅ mono-, di-, or polyether residue having from 1 to 14 oxygen atoms, and n is an integer.
 15. The dental adhesive according to any one of the preceding claims, wherein said polymerizable monomer is a mono-, bis- or poly(meth)acrylamide characterized by one of the following formulas:


16. The dental adhesive according to any one of the preceding claims, which contains polymerizable monomers of components (i) in an amount of from 5 to 90 wt-%.
 17. The dental adhesive according to any one of the preceding claims, wherein said polymerization initiator is a photo initiator such as camphor quinone.
 18. The dental adhesive according to any one of the preceding claims, which further contains an inorganic filler and/or an organic filler.
 19. Use of a thermal polymerisation inhibitor of formula (I) defined in any one of claims 1 or 2 in a one-part self-etching, self-priming dental adhesive having a pH of at most
 2. 